MECHANICAL PROPERTIES OF Cu SURFACE IN THE LAMINATED STRUCTURE OF Cr-Cu COATINGS

Tri Widodo Besar Riyadi(1*)

(1) Universitas Muhammadiyah Surakarta
(*) Corresponding Author

Abstract

A laminated structure of Cr-Cu coating was produced by electroplating on a carbon steel substrate. Two baths of chromium and copper electrolyte solutions were prepared to respectively deposit Cr and Cu as the first and second layer. The Cr was plated using the same plating time of 60 minutes, whereas Cu was deposit using plating time of 1 hour, 1.5 hours, 2 hours, 3 hours and 3.5 hours. The effect of plating time on the thickness, hardness and specific wear rate of the Cu surface was investigated. The formed phase, thickness, hardness and specific wear rate of the Cu surface were observed using XRD, optical microscope, Vickers microhardness tester and Ogoshi wear rate tester, respectively. The results show that Cu was formed on the surface. An increase of the Cu plating time increased the thickness and the specific wear rate of the Cu surface, but reduced the hardness of Cu surface. Cu layer was observed denser than that of Cr. This study showed that the use of Cu can be a potential candidate to laminate Cr for use in corrosive environment.  
Keywords

References

Ching An Huang, Chao Yu Che. Hardness variation and annealing behavior of a Cr– Ni multilayer electroplated in a trivalent chromium-based bath., Surface & Coatings Technology, pp. 203, 3320–3324, 2009.

Ching An Huang, Chao Yu Chen, Chun Ching Hsua and Chao Sung Lin. Characterization of Cr–Ni multilayers electroplated from a chromium(III)–nickel(II) bath using pulse current., Scripta Materialia, pp. 57, 61–64, 2007.

P. G. Keech, P. Vo, S. Ramamurthy, J. Chen, R. Jacklin and D. W. Shoesmith, Design and development of copper coatings for long term storage of used nuclear fuel, Corrosion Engineering, Science and Technology, Vol. 49 No. 6, pp. 425-430, 2014.

Jiaping Zhang, Xiaomei Feng, Yifu Shen, Cheng Chen, and Cuiyuan Duan, Microstructures and properties of Cr–Cu/W–Cu bi-layer composite coatings prepared by mechanical alloying, International Journal of Materials Research 107, 6, 544552, 2016.

E. Menthe, K. T. Rie, Plasma nitriding and plasma nitrocarburizing of electroplated hard chromium to increase the wear and the corrosion properties, Surface and Coatings Technology, pp. 112, 217–220, 1999.

Masyrukan, Tri Widodo Besar Riyadi, Bibit Sugito, dan Yudit Novianto, Effect of Immersion Time on the Deffect Formations and Properties of the Electroplating Chrome, Proceeding of The 2nd International Conference on Engineering Technology and Industrial Application (ICETIA 2015), Engineering for Creative Industry, page 111115, 15 Oktober 2015.

Tri Widodo Besar Riyadi, Masyrukan, Bibit Sugito, dan Tri Widodo, Pengaruh Waktu Tahan Celup Terhadap Nilai Kilap dan Ketebalan Lapisan Tembaga pada Proses Elektroplanting Baja Karbon Tinggi, Media Mesin, Vol. 15 No. 2 hal. 87-92, Juli 2014.

DOI: 10.23917/mesin.v18i1.3944

Article Metrics

Abstract view(s): 379 time(s)
PDF (Bahasa Indonesia): 316 time(s) PDF: 169 time(s)

Refbacks

  • There are currently no refbacks.