KARAKTERISASI SIFAT FISIS DAN MEKANIS PENGELASAN ALUMINIUM SERI AA-5052 DENGAN METODE FRICTION STIR WELDING, DENGAN FEED RATE 60 MM/MENIT PADA PUTARAN 1500 RPM DAN SUDUT KEMIRINGAN TOOLS 30 YANG DILANJUTKAN ANNEALING DAN NORMALIZING
BIbit Sugito(1*), Pramuko Ilmu Purbo Putro(2), Agus Dwi Anggono(3), Agung Setyo Darmawan(4), Masyrukan Masyrukan(5), Aditya Qomarudin(6)(1) Universitas Muhammadiyah Surakarta
(2) Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta
(3) Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta
(4) Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta
(5) Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta
(6) Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta
(*) Corresponding Author
Abstract
Tujuan penelitian ini untuk mengetahui pengaruh annealing dan normalizing dari pengelasan aluminium seri AA 5052 terhadap struktur mikro, tegangan tarik, dan kekerasan. Proses pengelasan dengan parameter feed rate 60 mm/menit, kemiringan tools 3º, kecepatan putar 1500 rpm. Hasil penelitian didapatkan kekuatan tarik raw material sebesar 162.54 MPa dengan regangan sebesar 8.61%, kekuatan tarik yang di annealing dan normalizing masing-masing 157.86 Mpa dengan regangan 7.41%, dan 141.66 Mpa dengan regangan 8.18 %. Sedangkan nilai kekerasan pada base metal sebesar 53.7 BHN, daerah HAZ 40.6 BHN, daerah lasan 30.4 BHN. Nilai kekerasan yang di annealing dan normalizing masing – masing sebesar 23.6 BHN pada raw material, HAZ 23.6 BHN daerah lasan 20.2 BHN, sedangkan yang normalizing 26.1 BHN, HAZ 22.7 BHN dan daerah lasan 21.6 BHN. Pada pengamatan struktur mikro perlakuan panas annealing dan normalizing mengalami penghalusan butir yang dapat dilihat pada foto terlihat mengecil dan merapat.
Keywords
Full Text:
PDF (Bahasa Indonesia)References
Adamowski, J., dan Szdoko, M. 2007. Friction Stir Welding (FSW) of Aluminium Alloy AW6082-T6. Volume 20. Journal of Achievements in Materials and Manufacturing Engineering. International OCSCO World Press
American Society for Metals Handbook Committee. 1990. Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, Volume 02. ASM International. The Materials Information Company.
American Society for Metals Handbook Committee, 1991, Heat Treating, Volume 04, ASM International, The Materials Information Company.
American Society for Metals Handbook Committee, 2004, Welding, Brazing, and Soldering, Volume 06, ASM International, The Materials Information Company.
American Society for Testing and Materials. 2003. Standard Test Methods for Tension Testing of Metallic Material, ASTM, E8M-04.
American Society for Metals Handbook Committee, 2004, Metallography and Microstructures, Volume 09, ASM International, The Materials Information Company.
Anggono, A. D., Riyadi, T. W. B., dkk., 2018 Influence of Tool Rotation and Welding Speed on The Friction Stir Welding of AA 1100 and AA 6061-T6, Teknik Mesin Universitas Muhammadiyah Surakarta.
Azom Materials – California Metal & Supply, Inc. 2012. Aluminium / Aluminium Alloy 5052 (UNS AA5052), https://www.azom.com/article.aspx?ArticleID=6615 , diakses pada 21 September 2018 pukul 12.24 WIB.
Dawes, C, J. 1999. Friction Stir Welding. TALAT Lecture 4410. The
Welding Institute. Cambridge.
Gunawan, S., 2016. Efek Perlakuan Panas Aging Terhadap Kekerasan dan Ketangguhan Impak Paduan Aluminium AA 514.0. Jurusan Teknik Mesin STTNas Yogyakarta.
Kamenichny, I. 1969. A Short Handbook of Heat Treatment. Mir Publishers. Moscow.
Mandal. 2005. Aluminum Welding. 2nd ed. Narosa Publishing House. New Delhi.
Mishra, R.S. dan Ma, Z.Y. 2005. Friction Stir Welding and Processing, Journal of Materials Science and Engineering. Science Direct.
Moarrefzadeh, Ali. 2012. Study of Heat Affected Zone (HAZ) in Friction
Welding Process. Iran: Journal of Mechanical Engineering.
Nandan, R, T. DebRoya, H.K.D.H. Bhadeshia. 2008. Recent Advances In Friction Stir Welding - Process, Weldment Structure and Properties. Science Direct.
Rajakumar, S., dan Balasubramanian, V. 2012. Correlation Between Weld Nugget Grain Size, Weld Nugget Hardness and Tensile Strength of Friction Stir Welded Commercial Grade Aluminium Alloy Joints.
Riswanda, Ilman, M., N., 2012, Studi Komparasi Sambungan Las Disamilar AA 5083 - AA 6061-T6 Antara TIG dan FSW, Industrial Research Workshop and National Seminar.
Riyatno, Sapto. 2014. Studi Pengelasan Friction Stir Welding Logam Tak Sejenis Antara ST.37 dan Aluminium AA 5052 dengsan pin Conus dan preheat. Surakarta : Universitas Sebelas Maret.
Romadhona, I., 2018, Studi Pengelasan Friction Stir Welding pada AA 1100 dengan Fe Menggunakan Variasi Feedrate 25 mm/menit, 30 mm/menit, dan 40 mm/menit, Tugas Akhir S-1, Universitas Muhammadiyah Surakarta.
Saputro, Toga A., 2014, Analisa Heat Treatment pada Aluminium Magnesium Silikon (Al-Mg-Si) dengan Silikon (1%, 3%, 5%) Terhadap Sifat Fisis dan Mekanis, Teknik Mesin Universitas Muhammadiyah Surakarta.
Setiawan, Idhar. H. 2018. Studi Pengelasan Friction Stir Welding (FSW) pada AA 6061-T6 dengan Fe Menggunakan Variasi Feedrate 30 mm/menit, 35 mm/menit, 40 mm/menit. Jurusan Teknik Mesin Universitas Muhammadiyah Surakarta.
Sidhu, Mandeep Singh. 2012. Friction Stir Welding-Process and its Variabels; A Review, International Journal of Emerging Technology and Advanced Engginering, India.
Subramaniam, Senthilkumar, dkk. 2012. Acoustic Emission–Based Monitoring Approach for Friction Stir Welding of Aluminum Alloy AA6063-T6 with Different Tool Pin. Journal of Engineering Manufacture. Institution of Mechanical Engineering. India.
Sugito, B., Anggono, D. A., Prasetyana, D., 2016, Pengaruh Kedalaman Pin (Depth Plunge) terhadap Kekuatan Sambungan Las pada Pengelasan Gesek AL 5083, Teknik Mesin Universitas Muhammadiyah Surakarta.
Surdia, Tata dan Saito, Shinroku. 2000. Pengetahuan Bahan Teknik. Jakarta: PT.Pradya Paramita.
Sydney, H.A.1974. Introduction to Physical Metalurgi. Mc Graw Hill Inc.
Prayogo, B., 2016, Analisa Sifat Mekanik dan Struktur Mikro Pada Proses Friction Stir Welding Aluminium 5052, Bandung : Universitas Jendral Achmad Yani.
Tim Pengajar Bahan Teknik. 2011. Materi Pembelajaran Mata Kuliah
Bahan Teknik I. Yogyakarta : Sekolah Vokasi, Universitas Gajah Mada.
Triyoko, D., 2016, Analisa Sifat Mekanik dan Struktur Mikro pada Sambungan Las Beda Properties Aluminium dengan Metode Friction Stir Welding, Teknik Mesin Universitas Muhammadiyah Surakarta.
Wiryosumarto, H., Okumura, T., 2000,Teknologi Pengelasan Logam, Jakarta: PT Pradya Paramita.